DESCRIPTION JP2004129044
The present invention provides a method for producing a textured corn paper. SOLUTION: A
material of fibers is used as a substrate of corn paper, an appropriate pattern is fixed to the
surface of a fiber substrate cloth with a polymer ink, and the substrate cloth is further
impregnated with a polymer resin, or a fiber First, the base fabric is impregnated with the
polymer resin, dried, and then patterned on the base fabric with a polymer ink, and a single
polymer resin is attached to the base body to form a clear color pattern. After drying, the
substrate cloth is processed into a predetermined cone shape using a mold at a higher
temperature and varnished on the surface of the cone and further trimmed to obtain a product.
As a result, a good pattern is formed on the surface of corn paper formed of fiber cloth, and the
aesthetics and texture of corn paper are enhanced. [Selected figure] Figure 1
Method for producing textured corn paper on the surface
[0001] The present invention relates to a method for producing a surface-patterned corn paper,
and in particular, a material of fibers is used as a corn paper base, and this flaky fibrous base is
used. An appropriate pattern is fixed to the surface of the cloth with a polymer ink, and the base
cloth is further impregnated with the polymer resin, or the fiber base cloth is first impregnated
with the polymer resin and then dried and further polymer. The substrate cloth is patterned with
ink to adhere one layer of polymer resin to the base body to form a clear color pattern, and after
drying, the base cloth is formed into a predetermined cone shape using a high-temperature mold.
The present invention relates to a manufacturing method for processing and varnishing the
surface of corn paper and trimming it to obtain corn paper having a color pattern on the surface.
2. Description of the Related Art In general, so-called cone paper is a kind of diaphragm, which
has a thin conical cylindrical structure and has an action of vibration transmission. It is attached
to a speaker in use, and when sound is transmitted, it passes through the cone paper, sound is
12-05-2019
1
effectively transmitted and can be heard by a person. Currently known corn paper is generally
made of fibers, such as pulp fibers, glass fibers, carbon fibers, and its production method is to
first process these fibrous materials into flakes and further put them in a mold. It is molded, dried
appropriately and trimmed to obtain a product. Corn paper formed of such known textiles is
uncolored on the surface and has no pattern or pattern on the surface. As a result, in the present
age where aesthetics and texture are lowered and novelty is required, consumers who seek high
quality are not satisfied with the demand, and thus there is a need for further creation for corn
paper quality design is there. SUMMARY OF THE INVENTION The main object of the present
invention is to provide a manufacturing method for effectively marking the surface of a type of
fibrous corn paper to enhance the texture and aesthetics of corn paper. It is in. According to the
invention of claim 1, in the method for producing a surface-patterned corn paper, a fiber material
cloth, for example, fibers of glass, kevlar, carbon, nomax, connex is used. It is used as a substrate
cloth of corn paper and printed on a fiber base fabric with a polymer ink, and a suitable pattern
of the polymer ink is fixed to the fiber base fabric, and the fiber base fabric is impregnated with a
polymer resin. First, the fiber base cloth is first impregnated with the polymer resin and then
dried, and then printed on the base cloth with the polymer ink, whereby one layer of polymer
resin is adhered to the fiber base body, and then dried. The polymer resin is effectively adhered
to the fiber base fabric, and the polymer resin is effectively bonded to the polymer ink, and the
color pattern definition is maintained, and the base fabric using a high temperature mold In the
prescribed cone paper shape A method for producing a textured corn paper characterized in that
it is processed and varnished on the surface of corn paper, dried and further trimmed to obtain a
textured corn paper product on the surface. .
FIG. 1 is a flow chart of the present invention. According to the present invention, a fiber material
cloth (e.g., glass, Kevlar, carbon, Nomax, Conex fibers) is used as a corn paper base cloth, and a
polymer ink as a fiber base Print on a cloth (of which the printing method is various printing
techniques such as screen printing, roller printing, spray printing, transfer printing, etc.) and fix
the appropriate pattern of the polymer ink to the fiber base cloth Furthermore, the fiber base
cloth is impregnated with the polymer resin (according to the flow of the present invention or as
shown in FIG. 2, the fiber base cloth is first impregnated with the polymer resin and then dried,
Printing on the substrate cloth with molecular ink, thereby depositing a layer of polymer resin on
the fiber substrate body, and drying appropriately (drying temperature is 40 ° C. to 120 ° C.,
time is about 5 minutes to 60) Between) or about 1 hour or several days and air-dried, effectively
adhered to fiber base cloth a polymer resin, and effectively is combined with a polymeric ink a
polymer resin, for holding the sharpness of the color pattern. Furthermore, the base cloth is
processed into a predetermined cone shape using a high temperature mold (type temperature is
120 ° C. to 200 ° C., time is 1 minute to 15 minutes), and varnished on the surface of corn
paper Dry properly (drying temperature is 40 ° C. to 80 ° C., time is about 10 minutes to 60
minutes), and the drying method is UV drying or natural drying and further trimming to obtain a
product. A very good pattern A is thus formed on the surface of the corn paper formed of the
12-05-2019
2
fiber cloth (see FIG. 3), and the aesthetics and texture of the corn paper are enhanced. After
completion of the above steps, one more coat of paint is applied (or not applied) and dried at 40
° C. to 80 ° C. for 10 minutes to 60 minutes to increase the surface gloss. According to the
present invention, the fiber material is used as a corn paper base, a suitable pattern is fixed to the
surface of the fiber base cloth with a polymer ink, and the base cloth is made high. The resin is
impregnated with a molecular resin, or the fiber base cloth is first impregnated with a polymer
resin and then dried, and then the base cloth is patterned with a polymer ink, and one polymer
resin is attached to the base body. And after drying, the substrate cloth is processed into a
predetermined cone shape using a high-temperature die, and varnished on the cone surface and
further trimmed to obtain a product. As a result, a good pattern is formed on the surface of corn
paper formed of fiber cloth, and the aesthetics and texture of corn paper are enhanced.
BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flowchart of the present invention. FIG. 2 is a
flow chart of another embodiment of the present invention. FIG. 3 is a view of the product of the
present invention. [Explanation of code] A pattern